ABSTRACT
Abstract: The aim of this study was to evaluate the tissue dissolution ability of different irrigating solutions associated or not to ultrasonic agitation. Ninety bovine pulp fragments (n=10 per group) were weighed and then placed individually in Eppendorf test tubes containing the following irrigants: G1- 2.5% sodium hypochlorite (NaOCl); G2- 2.5% NaOCl + ultrasonic agitation (US); G3- 2.5% NaOCl + 0.2% cetrimide (CTR); G4- 2.5% NaOCl + 0.2% CTR + US; G5- 400 ppm Sterilox (SX); G6- SX + US; G7- 0.2% CTR; G8- 0.2% CTR + US; G9- saline solution. Two blinded observers assessed the samples continuously for the first 4 h, and then every hour for the next 12 h. Dissolution speed was calculated by dividing the initial pulp weight (mg) by the period of time until complete dissolution (min). Data were compared by ANOVA and Tukey post hoc test with a 5% significance level. G1 to G4 dissolved pulp fragments completely and G2 was significantly faster than the other groups. G5 to G9 did not exhibit dissolving activity. In conclusion, only groups containing NaOCl were capable of pulp tissue dissolution, which was enhanced by ultrasonic agitation, but did not alter when 0.2% cetrimide was associated. This isolated solution and Sterilox showed no dissolving capacity, regardless the use of ultrasound.
Resumo: O objetivo deste estudo foi avaliar a capacidade de dissolução tecidual de diferentes soluções irrigadoras associadas ou não à agitação ultrassônica. Noventa fragmentos de polpa bovina (n=10 por grupo) foram pesados e em seguida colocados individualmente em tubos tipo Eppendorf contendo os seguintes irrigantes: G1- hipoclorito de sódio (NaOCl) a 2,5%; G2- NaOCl a 2,5% + agitação ultrassônica (US); G3- NaOCl a 2,5% + cetramida (CTR) a 0,2%; G4- NaOCl a 2,5% + CTR a 0,2% + US; G5- 400 ppm Sterilox (SX); G6- SX + US; G7- CTR a 0,2%; G8- CTR a 0,2% + US; G9- solução salina. Dois observadores cegados em relação aos grupos experimentais avaliaram as amostras continuamente durante as primeiras 4 h e depois a cada hora pelas próximas 12 h. A velocidade de dissolução foi calculada dividindo o peso inicial da polpa (mg) pelo período de tempo até sua dissolução completa (min). Os dados foram comparados por ANOVA e teste post hoc de Tukey com nível de significância de 5%. Os grupos G1 a G4 dissolveram os fragmentos de polpa completamente e G2 foi significativamente mais rápido do que os outros. Os grupos G5 a G9 não apresentaram atividade de dissolução. Em conclusão, apenas grupos contendo NaOCl foram capazes de dissolver tecido pulpar, o que foi melhorado pela agitação ultrassônica, mas não alterado quando CTR a 0,2% foi associada. Esta solução isolada e o Sterilox não mostraram nenhuma capacidade de dissolução, independentemente da utilização do ultrassom.
Subject(s)
Animals , Cattle , Dental Pulp , Root Canal Irrigants , UltrasonicsABSTRACT
The present study aimed to evaluate the influence of the following irrigating solutions on the microhardness of root canal dentin: 2% sodium hypochlorite (2NaOCl), 5% sodium hypochlorite (5NaOCl), super-oxidized water (400 ppm Sterilox - Sx) and 17% EDTA (E). Eighty roots from bovine incisors were randomly divided into 8 groups (n=10): 2NaOCl, 5NaOCl, Sx, and 2NaOCl + E, 5NaOCl + E, Sx + E (associated with E as final irrigant for 5 min), E solely and distilled water (dH2O) as the negative control. Root canal preparation was performed by hand instruments, using one of the irrigation protocols for 30 min. Then, 5 mm of the cervical root third were cut out from each sample and subjected to the Vickers microhardness test, at two points, one at approximately 500-1000 µm from the root canal lumen (distance 1), and the other at approximately 500-1000 µm from the external root surface (distance 2). Data were analyzed by Wilcoxon and Kruskal-Wallis tests at 5% significance level. Microhardness values at distance 1 were significantly lower than those at distance 2 for all groups, except 5NaOCl and 5NaOCl + E groups (p>0.05). EDTA showed the lowest microhardness values. However, no statistically significant difference was detected among groups at distance 1 and EDTA was significantly different only from Sx at distance 2. In conclusion, all tested solutions showed lower microhardness at the most superficial root canal dentin layer compared to the one found near the external root surface, except 5NaOCl and 5NaOCl + E; EDTA promoted lower microhardness values in comparison to Sterilox at this site.
O presente estudo teve como objetivo avaliar a influência das seguintes soluções irrigadoras na microdureza da dentina do canal radicular: hipoclorito de sódio a 2% (NaOCl2), hipoclorito de sódio a 5% (NaOCl5), água superoxidada (Sterilox(r) 400 ppm - Sx) e EDTA a 17% (E). Oitenta raízes de incisivos bovinos foram divididas aleatoriamente em 8 grupos (n=10): NaOCl2, NaOCl5, Sx e NaOCl2 + E, NaOCl5 + E, Sx + E (associados ao E como irrigante final por 5 min), E isolado e água destilada (H2Od), como controle negativo. O preparo dos canais radiculares foi realizado com instrumentos manuais, usando um dos protocolos de irrigação por 30 min. A seguir, 5 mm do terço cervical de cada amostra foram cortados perpendicularmente e submetidos ao teste de microdureza de Vickers, em dois pontos, um aproximadamente 500-1000 µm da luz do canal radicular (distância 1), e o outro aproximadamente 500-1000 µm da superfície externa da raiz (distância 2). Os dados foram analisados pelos testes de Wilcoxon e Kruskal-Wallis com um nível de significância de 5%. Os valores de microdureza na distância 1 foram significativamente menores do que na distância 2 para todos os grupos, exceto NaOCl5 e NaOCl5 +E (p>0,05). O EDTA mostrou os menores valores de microdureza. No entanto, não foi detectada diferença estatisticamente significativa entre os grupos na distância 1 e o EDTA foi significativamente diferente apenas do Sx na distância 2. Pode-se concluir que todas as soluções testadas mostraram menor microdureza na camada de dentina mais superficial do canal radicular em comparação aos valores encontrados próximo à superfície radicular externa, exceto NaOCl5 e NaOCl5 + E; o EDTA promoveu menor microdureza em comparação ao Sterilox(r) neste ponto.